Guillory, Roger J.

Platinum-containing stents are commonly used in humans with hypercholesterolemia, whereas preclinical stent evaluation has commonly been performed in healthy animal models, providing inadequate information about stent performance under hypercholesterolemic conditions. In this investigation, we used an ApoE−/− mouse model to test the impact of hypercholesterolemia on neointima formation on platinum-containing implants. We implanted 125 μm diameter platinum wires into the abdominal aortas of ApoE−/− and ApoE+/+ mice for 6 months, followed by histological and immunofluorescence examination of neointimal size and composition. It was found that ApoE−/− mice developed neointimas with four times larger area and ten times greater thickness than ApoE+/+ counterparts. Neointimas developed in the ApoE−/− mice also contained higher amounts of lipids quantified as having 370 times more coverage compared to ApoE+/+, a 3-fold increase in SMCs, and a 22-fold increase in macrophages. A confluent endothelium had regenerated in both mouse strains. The ApoE−/− mice experienced luminal reductions more closely resembling clinically relevant restenosis in humans. Overall, the response to platinum arterial implants was highly dependent upon the atherogenic environment.

OBJECTIVE Bioresorbable flow diverters (BRFDs) could significantly improve the performance of next-generation flow diverter technology. In the current work, magnesium and iron alloy BRFDs were prototyped and compared in terms of porosity/pore density, radial strength, flow diversion functionality, and resorption kinetics to offer insights into selecting the best available bioresorbable metal candidate for the BRFD application. METHODS BRFDs were constructed with braided wires made from alloys of magnesium (MgBRFD) or iron (FeBRFD). Pore density and crush resistance force were measured using established methods. BRFDs were deployed in silicone aneurysm models attached to flow loops to investigate flow diversion functionality and resorption kinetics in a simulated physiological environment. RESULTS The FeBRFD exhibited higher pore density (9.9 vs 4.3 pores/mm2) and crush resistance force (0.69 ± 0.05 vs 0.53 ± 0.05 N/cm, p = 0.0765, n = 3 per group) than the MgBRFD, although both crush resistances were within the range previously reported for FDA-approved flow diverters. The FeBRFD demonstrated greater flow diversion functionality than the MgBRFD, with significantly higher values of established flow diversion metrics (mean transit time 159.6 ± 11.9 vs 110.9 ± 1.6, p = 0.015; inverse washout slope 192.5 ± 9.0 vs 116.5 ± 1.5, p = 0.001; n = 3 per group; both metrics expressed as a percentage of the control condition). Last, the FeBRFD was able to maintain its braided structure for > 12 weeks, whereas the MgBRFD was almost completely resorbed after 5 weeks. CONCLUSIONS The results of this study demonstrated the ability to manufacture BRFDs with magnesium and iron alloys. The data suggest that the iron alloy is the superior material candidate for the BRFD application due to its higher mechanical strength and lower resorption rate relative to the magnesium alloy.

The use of flow diverters is a rapidly growing endovascular approach for the treatment of intracranial aneurysms. All FDA-approved flow diverters are composed of nitinol or cobalt-chromium, which will remain in the patient for the duration of their life. Bioresorbable flow diverters have been proposed by several independent investigators as the next generation of flow diverting devices. These devices aim to serve their transient function of occluding and healing the aneurysm prior to being safely resorbed by the body, eliminating complications associated with the permanent presence of conventional flow diverters. Theoretical advantages of bioresorbable flow diverters include (1) reduction in device-induced thrombosis; (2) reduction in chronic inflammation and device-induced stenosis; (3) reduction in side branch occlusion; (4) restoration of physiological vasomotor function; (5) reduction in imaging artifacts; and (6) use in pediatric applications. Advances made in the similar bioresorbable coronary stenting field highlight some of these advantages and demonstrate the feasibility and safety of bioresorbable endovascular devices in the clinic. The current work aims to review the progress of bioresorbable flow diverters, identify opportunities for further investigation, and ultimately stimulate the advancement of this technology.