Zhang, Tao

ABSTRACTThis study was to test our hypothesis that flexor tendon reconstruction with an allograft revitalized with bone marrow stromal cells (BMSCs) and synovialized with carbodiimide derivatized autologous synovial fluid (cd‐SYN) would result in better digit functional restoration than the conventional allograft tendon. A total of 32 flexor digital profundus tendons from the second and fifth digit of 16 dogs were created a repair failure model first. Then, failed‐repaired tendons were reconstructed with either a revitalized‐synovialized allograft tendon or a clinical standard autograft tendon (control group). The allograft tendon was seeded with autologous BMSCs in multiple slits and the graft surface was coated with cd‐SYN. A 6 weeks after tendon reconstruction, the digits were harvested and evaluated for digit function, adhesion status, tendon gliding resistance, attachment strength, cell viability, and histologic factors. The allograft group had significantly improved digit function compared with the control group through decreased work of flexion, increased digit range of motion under 2‐Newton force, and less adhesion score (p < .05). However, the distal attachment‐site strength and stiffness in the allograft tendon were significantly weaker than the autografts (p < .05). No significant difference was found for gliding resistance. Histologically, allograft tendons coated with allograft had smoother surfaces and showed tendon‐to‐bone and tendon‐to‐tendon incorporation. Viable BMSCs were found in the tendon slits 6 weeks after the graft. In conclusion, cellular lubricant‐based modification of allograft tendons improved digit function and reduced the adhesions compared with autograft for flexor tendon reconstruction. However, improvement of graft‐to‐host tendon healing is still challenging. © 2018 Orthopaedic Research Society. Published by Wiley Periodicals, Inc. J Orthop Res 36:2218–2227, 2018.

ABSTRACTSurgical repair is a common treatment for rotator cuff tear; however, the retear rate is high. A high degree of suture repair strength is important to ensure rotator cuff integrity for healing. The purpose of this study was to compare the mechanical performance of rotator cuffs repaired with a mesh suture versus traditional polydioxanone suture II and FiberWire sutures in a canine in vitro model. Seventy‐two canine shoulders were harvested. An infraspinatus tendon tear was created in each shoulder. Two suture techniques—simple interrupted sutures and two‐row suture bridge—were used to reconnect the infraspinatus tendon to the greater tuberosity, using three different suture types: Mesh suture, polydioxanone suture II, or FiberWire. Shoulders were loaded to failure under displacement control at a rate of 20 mm/min. Failure load was compared between suture types and techniques. Ultimate failure load was significantly higher in the specimens repaired with mesh suture than with polydioxanone suture II or FiberWire, regardless of suture technique. There was no significant difference in stiffness among the six groups, with the exception that FiberWire repairs were stiffer than polydioxanone suture II repairs with the simple interrupted technique. All specimens failed by suture pull‐out from the tendon. Based on our biomechanical findings, rotator cuff repair with the mesh suture might provide superior initial strength against failure compared with the traditional polydioxanone suture II or FiberWire sutures. Use of the mesh suture may provide increased initial fixation strength and decrease gap formation, which could result in improved healing and lower re‐tear rates following rotator cuff repair. © 2017 Orthopaedic Research Society. Published by Wiley Periodicals, Inc. J Orthop Res 36:987–992, 2018.