Mékidèche, Thibaut

Aims The aims of this study were to compare the mean duration of antibiotic release and the mean zone of inhibition between vancomycin-loaded porous tantalum cylinders and antibiotic-loaded bone cement at intervals, and to evaluate potential intrinsic antimicrobial properties of tantalum in an in vitro medium environment against methicillin-sensitive Staphylococcus aureus (MSSA). Materials and Methods Ten porous tantalum cylinders and ten cylinders of cement were used. The tantalum cylinders were impregnated with vancomycin, which was also added during preparation of the cylinders of cement. The cylinders were then placed on agar plates inoculated with MSSA. The diameter of the inhibition zone was measured each day, and the cylinders were transferred to a new inoculated plate. Inhibition zones were measured with a Vernier caliper and using an automated computed evaluation, and the intra- and interobserver reproducibility were measured. The mean inhibition zones between the two groups were compared with Wilcoxon’s test. Results MSSA was inhibited for 12 days by the tantalum cylinders and for nine days by the cement cylinders. At day one, the mean zone of inhibition was 28.6 mm for the tantalum and 19.8 mm for the cement group (p < 0.001). At day ten, the mean zone of inhibition was 3.8 mm for the tantalum and 0 mm for the cement group (p < 0.001). The porous tantalum cylinders soaked only with phosphate buffered solution showed no zone of inhibition. Conclusion Compared with cement, tantalum could release antibiotics for longer. Further studies should assess the advantages of using antibiotic-loaded porous tantalum implants at revision arthroplasty. Cite this article: Bone Joint J 2019;101-B:848–851.

ABSTRACTRevisions TKAs are being completed with uncemented constructs more frequently. We hypothesized that tantalum cones could be an efficient carrier of antibiotics in uncemented procedures. We aimed to compare the release of vancomycin between (i) tantalum and smooth stainless cylinders; (ii) different concentrations of vancomycin; and (iii) different durations of bathing. Specifically designed tantalum cylinders were bathed in a vancomycin solution with various durations of baths. We investigated rinses between each interval as well as the dose of vancomycin. Vancomycin concentrations were determined in each group by fluorescence polarization immunoassay at different intervals (1 h, days 1, 2, 3, 5). At 1 h, the mean vancomycin concentration for the 1‐hour soaking group was 3,172 μg/ml, whereas mean concentration for the smooth stainless steel group was 39.37 μg/ml (p < 0.001). The rinsing group showed a significantly lower concentration at 1 h and 1 day (p < 0.05). The 2‐gram vancomycin group showed no difference at days 1, 2, and 3 compared to the 1‐hour group. The 5, 15, and 30‐minute bathing groups showed significantly lower vancomycin concentrations at all‐time points. All vancomycin concentrations at day 3 were superior to the minimal inhibitory concentration of Staphyloccocus aureus. The mean concentration of vancomycin depends on the material, duration of bathing, the rinsing effect, and the drug dose. Our in‐vitro study is the first to show that porous tantalum cylinders allow antibiotic carriage and progressive release. If appearing in vivo, in a similar extent, this intrinsic property might be useful to prevent and/or treat peri‐prosthetic joint infection. © 2018 Orthopaedic Research Society. Published by Wiley Periodicals, Inc. J Orthop Res 37:308–312, 2019.