Nagiah, Naveen

Introduction: Myocardial infarction is an inflammatory condition that leads to scar deposition and cardiac remodeling. Stem cells (SC) are an alternative to prevent cardiac remodeling, but have poor survival after transplanted to an pro-inflammatory ischemic myocardium. Polymeric biocompatible scaffolds are biomaterials that can improve SC retention and survival, with the goal to improve regional cardiac function. Methods: We electrospun fibers of a) uniaxial polycaprolactone (PCL) and b) coaxial PCL (core) and gelatin methacrylate (sheath), an anti-inflammatory substance. We first tested the SC retention of each scaffold. Then, adipose derived mesenchymal SCs (MSCs) were co-cultured with M1 macrophages (pro-inflammatory) with and without scaffold and we measure the expression of inflammatory-related genes (RT-PCR). Lastly, PCL+GelMA scaffolds with and without MSCs (3.5x10 3 MSCs) were implanted after myocardial ischemia/reperfusion (IR) and followed for 2 weeks. Results: The average diameter of PCL and PCL+GelMA fibers were 730±40nm and 1110±50nm, respectively. PCL+GelMA scaffolds increased MSCs adhesion compared to PCL (absorbance: 0.09±.03 for PCL and 0.24±0.02 for coaxial, p<0.05). Figure A shows that MSCs in presence of M1 macrophages had a significant increase in inflammatory genes, which was significantly ameliorated in the presence of GelMA. In preliminary animal studies (n=1-4), MSCs delivered in a PCL+GelMA scaffold had partial preservation of regional function parameteres compared to IR only or IR+PCL+GelMA (no MSCs) (Figure B). Conclusion: Coaxially PCL+gelMA scaffolds attenuate the pro-inflammatory milieu of MSCs under ischemic-like conditions, and may improve regional cardiac remodeling.

AbstractStem cell−based therapies for various ailments have attracted significant attention for over a decade. However, low retention of transplanted cells at the damaged site has hindered their potential for use in therapy. Tissue engineered grafts with fibrillar structures mimicking the extracellular matrix (ECM) can be potentially used to increase the retention and engraftment of stem cells at the damaged site. Moreover, these grafts may also provide mechanical stability at the damaged site to enhance function and regeneration. Among all the methods to produce fibrillar structures developed in recent years, electrospinning is a simple and versatile method to produce fibrous structures ranging from a few nanometers to micrometers. Coaxial electrospinning enables production of a mechanically stable core with a cell‐binding sheath for enhanced cell adhesion and proliferation. Furthermore, this process provides an alternative to functionalized engineered scaffolds with specific compositions. The present article describes the protocol for developing a polycaprolactone (PCL) core and gelatin/gelatin methacrylate (GelMA) sheath laden with stem cells for various regenerative engineering applications. © 2021 Wiley Periodicals LLC.This article was corrected on 18 July 2022. See the end of the full text for details.Basic Protocol 1: Uniaxial PCL electrospinningBasic Protocol 2: Coaxial electrospinningSupport Protocol 1: Scaffold characterization for Basic Protocols 1 and 2Basic Protocol 3: Cell seeding on uniaxial and coaxial electrospun scaffolds and MTS assaySupport Protocol 2: Preparation of scaffold with cells for scanning electron microscopy