Lu, Lichun

The objective of our paper was to determine the effects of composite formulation on the compressive modulus and ultimate strength of a biodegradable, in situ polymerizable poly(propylene fumarate) (PPF) and bone fiber scaffold. The following parameters were investigated: the incorporation of bone fibers (either mineralized or demineralized), PPF molecular weight, N-vinyl pyrrolidinone (NVP) crosslinker amount, benzoyl peroxide (BP) initiator amount, and sodium chloride porogen amount. Eight formulations were chosen based on a resolution III two-level fractional factorial design. The compressive modulus and ultimate strength of these formulations were measured on a materials testing machine. Absolute values for compressive modulus varied from 21.3 to 271 MPa and 2.8 to 358 MPa for dry and wet samples, respectively. The ultimate strength of the crosslinked composites varied from 2.1 to 20.3 MPa for dry samples and from 0.4 to 16.6 MPa for wet samples. Main effects of each parameter on the measured property were calculated. The incorporation of mineralized bone fibers and an increase in PPF molecular weight resulted in higher compressive modulus and ultimate strength. Both mechanical properties also increased as the amount of benzoyl peroxide increased or the NVP amount decreased in the formulation. Sodium chloride had a dominating effect on the increase of mechanical properties in dry samples but showed little effects in wet samples. Demineralization of bone fibers led to a decrease in the compressive modulus and ultimate strength. Our results suggest that bone fibers are appropriate as structural enforcement components in PPF scaffolds. The desired orthopaedic PPF scaffold might be obtained by changing a variety of composite formulation parameters.

The objective of this study was to investigate the influence of pore geometry on the transport rate and depth after repetitive mechanical deformation of porous scaffolds for tissue engineering applications. Flexible cubic imaging phantoms with pores in the shape of a circular cylinder, elliptic cylinder, and spheroid were fabricated from a biodegradable polymer blend using a combined 3D printing and injection molding technique. The specimens were immersed in fluid and loaded with a solution of a radiopaque solute. The solute distribution was quantified by recording 20 μm pixel-resolution images in an X-ray microimaging scanner at selected time points after intervals of dynamic straining with a mean strain of 8.6 ± 1.6% at 1.0 Hz. The results show that application of cyclic strain significantly increases the rate and depth of solute transport, as compared to diffusive transport alone, for all pore shapes. In addition, pore shape, pore size, and the orientation of the pore cross-sectional asymmetry with respect to the direction of strain greatly influence solute transport. Thus, pore geometry can be tailored to increase transport rates and depths in cyclically deformed scaffolds, which is of utmost importance when thick, metabolically functional tissues are to be engineered.

Natural and synthetic hydrogels have attracted much attention for nerve regeneration. Previous studies have shown that electrical charge has significant effect on stimulation of neurite outgrowth. In this work, incorporation of a positively charged monomer into the photocrosslinkable oligo(polyethylene glycol) fumarate (OPF) hydrogel has been investigated. We have evaluated the effect of localized positive charge on neurite outgrowth in culture with an objective that positively charged hydrogels ultimately can be used for stimulating in vivo nerve regeneration. The effect of charged modification has been also studied on mechanical properties and swelling ratio of these hydrogels. Our data indicated that with increasing charge density hydrogels swelling ratio increased in water, however it remained constant in PBS. We also demonstrated that compressive modulus and tensile strength of the hydrogels improved with incorporation of electrical charge into the hydrogels. Biodegradation of modified hydrogels was investigated in a series of biomimetic solutions. OPF hydrogels appeared to be more susceptible to oxidative degradation as opposed to the hydrolytic degradation in enzymes and acidic solution, and the degradation rate was correlated to the PEG molecular weight and charge density of the hydrogels. To investigate the effect of charge modification on nerve cell attachment and differentiation, dissociated dorsal root ganglion (DRG) cells were plated onto the modified and unmodified hydrogels surfaces. DRG cells attached and extended their neurites more readily on the surface of positively charged hydrogels as opposed to the unmodified hydrogels.