Nabzdyk, Christoph S.

Objectives: In practice, midodrine has been used to reduce IV vasopressor requirements and decrease ICU length of stay. However, recent publications have failed to show clinical success when midodrine was administered every 8 hours. One possible reason for the lack of clinical efficacy at this dosing interval may be the pharmacokinetic properties of midodrine that support a more frequent dosing interval. Here, we report our institutional experience with midodrine at a dosing frequency of every 6 hours. Design: Single, quaternary academic medical center, retrospective, descriptive study. Setting: Floor and ICU patients admitted to Mayo Clinic, Rochester, from May 7, 2018, to September 30, 2020. Patients: Adult patients with an order for midodrine with a dosing frequency of “every 6 hours” or “four times daily” were eligible for inclusion. Interventions: No intervention performed. All data were abstracted retrospectively from the electronic medical record. Measurements and Main Results: Forty-four unique patients were identified that met inclusion criteria. Patients were an average of 65 years and 63.6% were male. The individual doses of midodrine ranged from 5 to 20 mg. Twenty-three patients (52.3%) were receiving IV vasopressors at the time midodrine was ordered every 6 hours. Vasopressor requirements decreased from an average of 0.10 norepinephrine equivalents 24 hours prior to the every 6-hour order to 0.05 norepinephrine equivalents 24 hours after an order for midodrine every 6 hour was placed. Conclusions: Increasing the dosing frequency of midodrine to every 6 hours may optimize its pharmacokinetic profile without compromising safety. This midodrine dosing frequency should be prospectively evaluated as a primary strategy for accelerated IV vasopressor wean.

AbstractFor decades, bioadhesive materials have garnered great attention due to their potential to replace sutures and staples for sealing tissues during minimally invasive surgical procedures. However, the complexities of delivering bioadhesives through narrow spaces and achieving strong adhesion in fluid‐rich physiological environments continue to present substantial limitations to the surgical translation of existing sealants. In this work, a new strategy for minimally invasive tissue sealing based on a multilayer bioadhesive patch, which is designed to repel body fluids, to form fast, pressure‐triggered adhesion with wet tissues, and to resist biofouling and inflammation is introduced. The multifunctional patch is realized by a synergistic combination of three distinct functional layers: i) a microtextured bioadhesive layer, ii) a dynamic, blood‐repellent hydrophobic fluid layer, and iii) an antifouling zwitterionic nonadhesive layer. The patch is capable of forming robust adhesion to tissue surfaces in the presence of blood, and exhibits superior resistance to bacterial adhesion, fibrinogen adsorption, and in vivo fibrous capsule formation. By adopting origami‐based fabrication strategies, it is demonstrated that the patch can be readily integrated with a variety of minimally invasive end effectors to provide facile tissue sealing in ex vivo porcine models, offering new opportunities for minimally invasive tissue sealing in diverse clinical scenarios.

AbstractThromboembolic and infectious complications stemming from the use of cardiovascular medical devices are still common and result in significant morbidity and mortality. There is no strategy to date that effectively addresses both challenges at the same time. Various surface modification strategies (e.g., silver, heparin, and liquid‐impregnated surfaces) are proposed yet each has several limitations and shortcomings. Here, it is shown that the incorporation of an ultrathin and mechanically robust hydrogel layer reduces bacterial adhesion to medical‐grade tubing by 95%. It is additionally demonstrated, through a combination of in vitro and in vivo tests, that the hydrogel layer significantly reduces the formation and adhesion of blood clots to the tubing without affecting the blood's intrinsic clotting ability. The adhesion of clots to the tubing walls is reduced by over 90% (in vitro model), which results in an ≈60% increase in the device occlusion time (time before closure due to clot formation) in an in vivo porcine model. The advantageous properties of this passive coating make it a promising surface material candidate for medical devices interfacing with blood.

Significance Owing to potential advantages including ease of use, airtight or watertight sealing, and minimal tissue damage, bioadhesives have been intensively studied and developed as an alternative to sutures and staples to close wounds, achieve hemostasis, and attach and immobilize implantable devices. However, existing bioadhesives have limitations including slow adhesion formation, weak bonding, low biocompatibility, poor mechanical match with tissues, and/or lack of triggerable benign detachment. In this work, we report a bioadhesive capable of instant tough adhesion and triggerable benign detachment that can potentially address all the above-mentioned limitations. The current work not only develops a bioadhesive with superior performances but also advances the understanding of wet adhesion.

Abstract Slippery and hydrophilic surfaces find critical applications in areas as diverse as biomedical devices, microfluidics, antifouling, and underwater robots. Existing methods to achieve such surfaces rely mostly on grafting hydrophilic polymer brushes or coating hydrogel layers, but these methods suffer from several limitations. Grafted polymer brushes are prone to damage and do not provide sufficient mechanical compliance due to their nanometer‐scale thickness. Hydrogel coatings are applicable only for relatively simple geometries, precluding their use for the surfaces with complex geometries and features. Here, a new method is proposed to interpenetrate hydrophilic polymers into the surface of diverse polymers with arbitrary shapes to form naturally integrated “hydrogel skins.” The hydrogel skins exhibit tissue‐like softness (Young's modulus ≈ 30 kPa), have uniform and tunable thickness in the range of 5–25 µm, and can withstand prolonged shearing forces with no measurable damage. The hydrogel skins also provide superior low‐friction, antifouling, and ionically conductive surfaces to the polymer substrates without compromising their original mechanical properties and geometry. Applications of the hydrogel skins on inner and outer surfaces of various practical polymer devices including medical tubing, Foley catheters, cardiac pacemaker leads, and soft robots on massive scales are further demonstrated.